Monolith MH 998-3
Monolith® MH 998-3 is used as an adhesive for firmly seating bearings and fixing and sealing cylindrical fits under dynamic and thermal stress.
The ordering process is carried out in an encrypted SSL connection.
Guaranteed by a valid certificate issued by nazwa.pl Sp. z o.o. (Security Guarantee).
Free shipping on purchases of PLN 500 or equivalent.
The right to return intact within 14 days.
Monolith® MH 998-3 belongs to the group of one-component, anaerobically cured, solvent-free products, i.e. after isolating the access of air (oxygen). An additional element in the curing mechanism is the catalytic action of the metal, therefore these adhesives can be used for joints in contact with the metal. The strength of the connection achieved and the polymerization time depends on the type of metal. Thus, in the presence of copper or brass, a very quick hardening occurs, but in turn the strength is 40% of that found on structural steel. The main applications of anaerobic adhesives are securing threads, nuts and pins against loosening, sealing threads and flat surfaces, and fixing all types of mating connections. Resistance to vibrations, shocks as well as to chemical media make them applicable both in repairs and renovations as well as on production lines.
Monolith® MH 998-3 is used as an adhesive for firmly seating bearings and fixing and sealing cylindrical fits under dynamic and thermal stress.
By filling with glue, the play between the bearing and the seat is eliminated. Newly designed devices can accommodate bearings with controlled clearance and less machining precision, achieving equal-fit joints. MONOLITH fills in all surface irregularities, giving 100% adhesion, which increases the friction force in the joint up to 3 times the value. Thanks to this, by choosing a "strong" Monolith, it is possible to obtain a connection transmitting very high torsional moments. It is often possible to abandon a fitted connection in favor of a sliding one. A suitable Monolith can replace the soldering technique, e.g. on sleeve joints of copper installations.
Strength class: high - difficult to disassemble.
Packaging:
50g - bottle
250g - bottle
A6390017CB
Data sheet
- Color
- green
- Viscosity [mPa · s]
- 2200-3400tx
- Thermal resistance [°C]
- -50 / +200
- Maximum gap or thread [mm]
- 0,10-0,30 / M36
- Shear strength [N/mm²]
- 26-45
- Breakaway torque [Nm]
- 28-48
- Curing time [godz.]
- 12
- Time to reach initial strength [min]
- 20-40
- Application area
- do połączeń cylindrycznych, wysoka