Monolith MH 995-3

Monolith® MH 995-3 is used as an adhesive for firmly seating bearings, fixing and sealing cylindrical fits under dynamic stress.

Package: 10 g

redeem
No reward points for this product.


  The ordering process is carried out in an encrypted SSL connection.

Guaranteed by a valid certificate issued by nazwa.pl Sp. z o.o. (Security Guarantee).

 

Free shipping on purchases of PLN 500 or equivalent.

  The right to return intact within 14 days.

Monolith® MH 995-3 belongs to the group of one-component, anaerobically cured, solvent-free products, i.e. after cutting off the access of air (oxygen). An additional element in the curing mechanism is the catalytic action of the metal, therefore these adhesives can be used for joints in contact with the metal. The strength of the connection achieved and the polymerization time depends on the type of metal. Thus, in the presence of copper or brass, a very quick hardening occurs, but in turn the strength is 40% of that found on structural steel. The main applications of anaerobic adhesives are securing threads, nuts and pins against loosening, sealing threads and flat surfaces, and fixing all types of mating connections. Resistance to vibrations, shocks as well as to chemical media make them applicable both in repairs and renovations as well as on production lines.

Monolith® MH 995-3 is used as an adhesive for firmly seating bearings and for fixing and sealing cylindrical fits under dynamic stress.

By filling with glue, the play between the bearing and the seat is eliminated. In the newly designed devices, it is possible to embed bearings with controlled clearance and lower machining accuracy, obtaining equal joints with pressed-in joints. MONOLITH fills in all surface irregularities, giving 100% adhesion, which increases the friction force in the joint up to 3 times the value. Thanks to this, by choosing a strong Monolith, it is possible to obtain a connection that transfers very high torsional moments. It is often possible to abandon a fitted connection in favor of a sliding one. A suitable Monolith can replace the soldering technique, e.g. on sleeve joints of copper installations.

Strength class: high - difficult to disassemble.

Packaging:

    50g - bottle
    250g - bottle

A64800002CB

Data sheet

Color
green
Viscosity [mPa · s]
400-800
Thermal resistance [°C]
-50 / +200
Maximum gap or thread [mm]
0,05-0,15 / M20
Shear strength [N/mm²]
25-44
Breakaway torque [Nm]
25-43
Curing time [godz.]
12
Time to reach initial strength [min]
15-30
Application area
termicznie odporny, do połączeń cylindrycznych