Monolith MH 585-3
Monolith MH 585-3 is an adhesive for securing bolts and nuts against loosening, as well as for sticking pins. Connections ensure absolute tightness and protect against corrosion. As the adhesive fills the space between the threads completely, the load is distributed over the entire length of the joint, preventing material fatigue.
Guaranteed by a valid certificate issued by nazwa.pl Sp. z o.o. (Security Guarantee).
and the date based on the PROFORMA invoice.
Monolith® MH 585-3 belongs to the group of one-component products, free of solvents, anaerobically cured, i.e. after shutting off the access of air (oxygen). An additional element in the curing mechanism is the catalytic action of the metal, therefore these adhesives can be used for joints in contact with the metal. The strength of the connection achieved and the polymerization time depends on the type of metal. Thus, in the presence of copper or brass, a very quick hardening occurs, but in turn the strength is 40% of that found on structural steel. The main applications of anaerobic adhesives are securing threads, nuts and pins against loosening, sealing threads and flat surfaces, and fixing all types of mating connections. Resistance to vibrations, shocks as well as to chemical media make them applicable both in repairs and renovations as well as on production lines.
Monolith® MH 585-3 is used as an adhesive for securing bolts and nuts against loosening, as well as for gluing studs. Connections ensure absolute tightness and at the same time protect against corrosion. As the adhesive completely fills the space between the threads, the load is distributed over the entire length of the joint, preventing material fatigue.
Strength class: high - difficult to dismantle.
10g - bottle
50g - bottle
250g - bottle
- Viscosity [mPa · s]
- Thermal resistance [°C]
- -55 / +150
- Maximum gap or thread [mm]
- 0,25 / M36
- Shear strength [N/mm²]
- Breakaway torque [Nm]
- Curing time [godz.]
- Time to reach initial strength [min]
- Application area
- zabezpieczanie gwintów i śrub, trudnodemontowalny